Cleaner forms of energy are needed, and H2 produced from water spliFng is a possible source. However, a robust catalyst is necessary to carry out the water oxidaKon reacKon. Plants uKlize Photosystem II to catalyze water oxidaKon as a part of photosynthesis, and many syntheKc water oxidaKon catalysts use Photosystem II as a model. In this study, the catalyst of interest was [(terpy)Mn(mu-O)2Mn(terpy)]3+ (MnTD), which was synthesized in a chromium-based Metal Organic Framework (MOF) to avoid degradaKon of MnTD molecules. Hard X-ray powder diffracKon was the primary method of analysis. The diffracKon data was used to detect the presence of MOF in samples at different catalyKc stages, and laFce parameters were assigned to the samples containing MOF. Fourier maps were constructed to determine the contents of the MOF as preliminary studies suggested that MnTD may not be present. Results showed that MOF is present before catalysis occurs, but disappears in the iniKal stages of catalysis. Changes in the MOF's laFce parameters suggest aWracKve interacKons between the MOF and catalyst; these interacKons may lead to the observed MOF degradaKon. Fourier maps also reveal limited, if any, amounts of MnTD in the system. Molecular manganese oxide may be the source of the high rate of water oxidaKon catalysis in the studied system. Show Partial Abstract